- 对靶磁控溅射制备VO_x薄膜及其退火研究
- Preparation of VO_x thin films by facing targets magnetron sputtering and study on anneailng of films
- 传感器与微系统 2007年第7期页码：54-57
- 作者机构：
  
  1. 天津大学电子信息工程学院
  2. 天津大学电子信息工程学院,天津,300072
- 作者简介：
- 基金信息：
  
  天津市自然科学基金资助项目（043600811）
- DOI：10.13873/j.1000-97872007.07.034
  中图分类号： TB383.2
- 纸质出版：2007
- 稿件说明：
移动端阅览
[1]韩雷,胡明,吕宇强,梁继然,刘志刚.对靶磁控溅射制备VO_x薄膜及其退火研究[J].传感器与微系统,2007(07):54-57.

HAN Lei, HU Ming, Lü Yu-qiang, et al. Preparation of VO_x thin films by facing targets magnetron sputtering and study on anneailng of films[J]. 2007, (7): 54-57.
[1]韩雷,胡明,吕宇强,梁继然,刘志刚.对靶磁控溅射制备VO_x薄膜及其退火研究[J].传感器与微系统,2007(07):54-57. DOI： 10.13873/j.1000-97872007.07.034.

HAN Lei, HU Ming, Lü Yu-qiang, et al. Preparation of VO_x thin films by facing targets magnetron sputtering and study on anneailng of films[J]. 2007, (7): 54-57. DOI： 10.13873/j.1000-97872007.07.034.

摘要

利用对靶磁控溅射法在玻璃基片上制备VOx薄膜

采用正交实验方法研究了镀膜条件对VOx薄膜电阻温度系数（TCR）的影响

得到优化的镀膜工艺参数

主要包括Ar∶O2为48∶0.4、工作压力恒定为2 Pa、基底的温度为室温27℃、溅射功率保持在180W

在此基础上

进行不同温度条件的真空退火

得到薄膜TCR在-2.5%

4.5%范围。利用原子力显微镜（AFM）和X射线光电子能谱法（XPS）分析了退火对提高薄膜TCR的作用

并找出VOx薄膜阻值与TCR的优化组合。同时

还观察到薄膜表面形貌的变化以及退火后薄膜中VO2

V2O3

V2O5的比例变化情况

并对其机理进行解释。

Abstract

Vanadium oxide thin films deposited on slide glass substrates are prepared by facing-target magnetron sputtering.The effect of sputtering conditions on temperature coefficient of resistance（TCR） is analyzed by orthogonal experiment

and the optimum process recipes are achieved

including Ar∶O2=48∶0.4

gas pressure is 2 Pa

substrate temperature is 27 ℃

sputtering power is 180 W.The TCR is improved to-2.5 %～-4.5 % after anneal at different temperature.The effect of anneal on TCR is analyzed by means of combined use of atomic force microscopes（AFM） and X-ray photoelectron spectroscopy（XPS） technique

while choosing the optimal combination of the resistance and TCR.The proportion changing of VO2

V2O3 and V2O5 and the surface transformation of the films after anneal are observed and explained.

关键词

Keywords

references

Reactive Ion Beams Sputtering of Vanadium Oxides Films for Uncooled Microbolometer [J] . Hongchen Wang,Xinjian Yi,Sihai Chen,Shaowei He,Xiaochao Fu. International Journal of Infrared and Millimeter Waves . 2005 (3)

Preparation of homogeneous VO X thin films by ion beam sputtering and annealing process [J] . S.B. Wang,S.B. Zhou,X.J. Yi. Vacuum . 2004 (1)

Excited state dynamics and semiconductor-to-metallic phase transition of VO 2 thin film [J] . Journal of Luminescence . 2004 (1)

Optimum oxygen concentration for the optoelectronic properties of IR sensitive VO x thin films [J] . K.M. Park,S. Yi,S. Moon,S. Im. Optical Materials . 2001 (1)

The structural characteristics of VO x films prepared by He-introduced reactive RF unbalanced magnetron sputtering [J] . H. Miyazaki,F. Utsuno,Y. Shigesato,I. Yasui. Thin Solid Films . 1996

浏览量

143

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

高温再生光纤光栅温度传感器封装技术

微型薄膜锂离子电池正极材料LiCoO₂薄膜研究

高温薄膜传感器制备与性能研究

微F-P腔可调谐滤波器关键工艺研究

NiCrAlY薄膜应变计的研制

对靶磁控溅射制备VOx薄膜及其退火研究

Preparation of VOx thin films by facing targets magnetron sputtering and study on anneailng of films

DOI：10.13873/j.1000-97872007.07.034

摘要

Abstract

关键词

Keywords

references

对靶磁控溅射制备VO_x薄膜及其退火研究

Preparation of VO_x thin films by facing targets magnetron sputtering and study on anneailng of films