研究与探讨 | 更新时间：2025-09-11

- ZrO₂氧传感器封接料开裂失效分析及改进
- Failure analysis and improvement of sealing material crack of ZrO₂ oxygen sensor
- 传感器与微系统 2018年第4期页码：38-40
- 作者机构：
  
  中国电子科技集团公司第四十九研究所
- 作者简介：
- 基金信息：
- DOI：10.13873/J.1000-9787(2018)04-0038-03
  中图分类号： TP212
- 纸质出版：2018
- 稿件说明：
移动端阅览
刘智敏, 秦浩, 王洋洋, 等. ZrO₂氧传感器封接料开裂失效分析及改进[J]. 传感器与微系统, 2018,(4):38-40.

LIU Zhi-min, QIN Hao, WANG Yang-yang, et al. Failure analysis and improvement of sealing material crack of ZrO₂ oxygen sensor[J]. 2018, (4): 38-40.
刘智敏, 秦浩, 王洋洋, 等. ZrO₂氧传感器封接料开裂失效分析及改进[J]. 传感器与微系统, 2018,(4):38-40. DOI： 10.13873/J.1000-9787(2018)04-0038-03.

LIU Zhi-min, QIN Hao, WANG Yang-yang, et al. Failure analysis and improvement of sealing material crack of ZrO₂ oxygen sensor[J]. 2018, (4): 38-40. DOI： 10.13873/J.1000-9787(2018)04-0038-03.

摘要

针对氧化锆（ZrO

）氧传感器封接料失效机理

提出了在传感器加热电路上增加预热功能

通过仿真和试验的方法验证了改进措施的有效性。仿真分析的结果表明:温度变化幅度为200℃时应力状态较温度变化400℃时的应力降低幅度约为40%。通过试验样件验证表明

传感器在进行了576次启动热应力试验后

封接料状态良好

未开裂

表明加热电路增加预热功能后降低了热应力冲击强度

增加预热电路后

传感器有效避免了使用中出现封接料开裂故障。

Abstract

According to failure mechanism of sealing material of ZrO

oxygen sensor

preheating function is put forward to add in sensor heating circuit. The effectiveness of the improved measure is verified by simulation and experiment.The results of simulation analysis show that the stress is reduced about 40% from temperature change range 200 ℃ to 400 ℃.The sample test results show that

after 576 times starting thermal stress tests are carried out

the sealing material is in good condition

without cracks.The results show that heating circuit can reduce the thermal stress impact strength after adding preheating function

which can avoid sealing material cracking in sensor usage.

关键词

Keywords

references

浏览量

119

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

热真空试验对极限电流型氧气传感器性能影响分析

过渡层对片式开关型汽车氧传感器性能的影响

ZrO₂氧气传感器加热电极漂移分析及改进研究

MEMS惯性器件的主要失效模式和失效机理研究

极限电流型氧气传感器动态测量与计算

ZrO2氧传感器封接料开裂失效分析及改进

Failure analysis and improvement of sealing material crack of ZrO2 oxygen sensor

DOI：10.13873/J.1000-9787(2018)04-0038-03

摘要

Abstract

关键词

Keywords

references

ZrO₂氧传感器封接料开裂失效分析及改进

Failure analysis and improvement of sealing material crack of ZrO₂ oxygen sensor