- 丙酮气体传感器的PANI/Au/Al₂O₃电极制备工艺优化
- Process optimization for preparing acetone gas sensor based on PANI / Au / Al₂O₃ electrode
- 传感器与微系统 2016年35卷第9期页码：66-68
- 作者机构：
  
  1. 成都大学生物工程学院
  2. 台湾勤益科技大学化工与材料工程系
- 作者简介：
- 基金信息：
  
  台湾科学委员会项目（NSC101-2221-E-167-027-MY3）;四川省教育厅科研项目（15ZB0378）;成都大学校青年基金资助项目（2015XJZ02）
- DOI：10.13873/J.1000-9787(2016)09-0066-03
  中图分类号： O657.1;TP212
- 纸质出版：2016
- 稿件说明：
移动端阅览
[1]刘文龙,李俊霞,易攀婷,杜景顺,郭升赢,张崟.丙酮气体传感器的PANI/Au/Al_2O_3电极制备工艺优化[J].传感器与微系统,2016,35(09):66-68.

LIU Wen-long, LI Jun-xia, YI Pan-ting, et al. Process optimization for preparing acetone gas sensor based on PANI / Au / Al₂O₃ electrode[J]. 2016, 35(9): 66-68.
[1]刘文龙,李俊霞,易攀婷,杜景顺,郭升赢,张崟.丙酮气体传感器的PANI/Au/Al_2O_3电极制备工艺优化[J].传感器与微系统,2016,35(09):66-68. DOI： 10.13873/J.1000-9787(2016)09-0066-03.

LIU Wen-long, LI Jun-xia, YI Pan-ting, et al. Process optimization for preparing acetone gas sensor based on PANI / Au / Al₂O₃ electrode[J]. 2016, 35(9): 66-68. DOI： 10.13873/J.1000-9787(2016)09-0066-03.

摘要

以微制程技术及电化学法制备PANI/Au/Al2O3电极

并组装成电阻式丙酮气体传感器。以恒电流法在不同电流密度下进行三阶段聚合

并利用混合物实验设计法对纳米结构PANI/Au/Al2O3电极的最佳制备工艺条件进行了优化。结果表明:分别固定聚合电流密度为40

80μA/cm2进行三阶段聚合

当聚合电流密度按由小到大顺序

所得的PANI/Au/Al2O3电极稳定性最好。固定聚合电量为35 m C

当三阶段电量比为0.35∶0.33∶0.32时

对于9 958×10-6丙酮得到最大的感测电阻变化率为7.55%。丙酮气体浓度在（475

189）×10-6与（23

18）×10-6范围内

对应灵敏度分别为1.2×10-3和6.4×10-3%/10-6

平均响应时间为3 min。

Abstract

In order to obtain a better performance of resistive acetone gas sensor

based on micro process technology and electrochemical methods

PANI / Au / Al2O3 electrode is prepared and assembled.Three-phase polymerization is carried out with different current density.Use mixture experimental design method

preparation process of nanostructure of PANI / Au / Al2O3 electrode is optimized.Results show that the stability of PANI / Au /Al2O3 electrode is the best when polymerization current density is fixed at 40

60 and 80 μA / cm2

respectively

and the aggregate current density chan

ge from small to large.Maintaining polymerization charge at 35 m C

as threephase charge ratio is 0.35 ∶ 0.33 ∶ 0.32

the maximum sensor resistance rate of the 9 958 × 10-6acetone is7.55 %.As the acetone gas concentration in the range of（475

1 189） × 10-6and（23

118） × 10-6

corresponding sensitivities are 1.2 × 10-3and 6.4 × 10-3% /10-6

and the average response time is 3 min.

关键词

Keywords

references

Effect of dopant concentration on polyaniline for hydrazine detection [J] . Kavirajaa Pandian Sambasevam,Sharifah Mohamad,Sook-Wai Phang. Materials Science in Semiconductor Processing . 2015

A carbon nanotube sensor array for sensitive gas discrimination using principal component analysis [J] . Yijiang Lu,Christina Partridge,M. Meyyappan,Jing Li. Journal of Electroanalytical Chemistry . 2006 (1)

Doped and dedoped polyaniline nanofiber based conductometric hydrogen gas sensors [J] . A.Z. Sadek,W. Wlodarski,K. Kalantar-Zadeh,C. Baker,R.B. Kaner. Sensors & Actuators: A. Physical . 2006 (1)

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于光化学沉积WO₃多孔薄膜的气体传感器研究

基于金属有机框架化合物的气体传感器研究进展

甲/乙醇气体传感器的研究进展

基于13X型沸石分子筛的类神经毒气传感器

烧结气氛对SnO₂纳米材料气敏性影响的研究

丙酮气体传感器的PANI/Au/Al2O3电极制备工艺优化

Process optimization for preparing acetone gas sensor based on PANI / Au / Al2O3 electrode

DOI：10.13873/J.1000-9787(2016)09-0066-03

摘要

Abstract

关键词

Keywords

references

丙酮气体传感器的PANI/Au/Al₂O₃电极制备工艺优化

Process optimization for preparing acetone gas sensor based on PANI / Au / Al₂O₃ electrode