碳纳米管为前驱体制备NiFe<sub>2</sub>O<sub>4</sub>及丙酮气敏性能研究

马冬则; 王亚玲; 陈辉; 林万明; 田林海

Chinese

您当前的位置：

首页 >

文章列表页 >

碳纳米管为前驱体制备NiFe₂O₄及丙酮气敏性能研究

研究与探讨 | 更新时间：2026-04-17

- 碳纳米管为前驱体制备NiFe₂O₄及丙酮气敏性能研究
- Preparation of NiFe₂O₄ using CNTs as precursor and study on its acetone gas-sensing properties*
- 传感器与微系统 2026年45卷第4期页码：12-16
- 作者机构：
  
  山西电子科技学院新能源与材料工程学院,山西,临汾,041000
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TP212
- 纸质出版：2026
- 稿件说明：
移动端阅览
马冬则, 王亚玲, 陈辉, 等. 碳纳米管为前驱体制备NiFe₂O₄及丙酮气敏性能研究[J]. 传感器与微系统, 2026,45(4):12-16.

MA Dongze, WANG Yaling, CHEN Hui, et al. Preparation of NiFe₂O₄ using CNTs as precursor and study on its acetone gas-sensing properties*[J]. 2026, 45(4): 12-16.
马冬则, 王亚玲, 陈辉, 等. 碳纳米管为前驱体制备NiFe₂O₄及丙酮气敏性能研究[J]. 传感器与微系统, 2026,45(4):12-16. DOI：

MA Dongze, WANG Yaling, CHEN Hui, et al. Preparation of NiFe₂O₄ using CNTs as precursor and study on its acetone gas-sensing properties*[J]. 2026, 45(4): 12-16. DOI：

摘要

利用溶剂热法合成碳纳米管(CNTs)-Ni/Fe前驱体复合物，对其进行焙烧得到NiFe

。通过扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)和N

-物理吸附仪对样品的微观形貌、晶体结构和比表面积进行了详细表征。随后，将上述材料制成传感器，对丙酮进行气敏性能测试。实验结果表明：当掺杂40mg CNTs在600℃下焙烧得到NiFe

，该传感器在270℃下对体积分数为100×10

-6

丙酮的响应值为48.5，是纯NiFe

传感器响应值的2倍，具有更加优异的气体敏特性。

Abstract

Carbon nanotubes(CNTs)-Ni/Fe precursor composites are synthesized by the solvothermal method and calcined to obtain NiFe

.The micromorphology

crystal structure and specific surface area of the samples are characterized in detail by scanning electron microscopy(SEM)

transmission electron microscopy(TEM)

X-ray diffractometer(XRD)and N

-physical adsorption analyzer.Subsequently

the above materials are made into sensors to test the gas-sensing properties for acetone.Experimental results show that the sensor based on NiF

which is doped with 40mg and calcined at 600℃

exhibits a response value of 48.5 toward to acetone with a volume fraction of 100×10

-6

at 270℃

which is twice that of the pure NiFe

sensor and has better gas-sensing properties.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于光化学沉积WO₃多孔薄膜的气体传感器研究

基于复合气敏材料WO₃/SrAl₂O₄的硫化氢气体传感器

丙酮气体传感器的PANI/Au/Al₂O₃电极制备工艺优化

CeO₂掺杂对ZnO薄膜气敏特性的影响

基于催化转化间接测量丙酮体积分数的方法

碳纳米管为前驱体制备NiFe2O4及丙酮气敏性能研究

Preparation of NiFe2O4 using CNTs as precursor and study on its acetone gas-sensing properties*

DOI：

摘要

Abstract

关键词

Keywords

references

碳纳米管为前驱体制备NiFe₂O₄及丙酮气敏性能研究

Preparation of NiFe₂O₄ using CNTs as precursor and study on its acetone gas-sensing properties*